Physics > Applied Physics
[Submitted on 8 Nov 2018]
Title:MOVPE growth of nitrogen- and aluminum-polar AlN on 4H-SiC
View PDFAbstract:We present a comprehensive study on metal-organic vapor phase epitaxy growth of N-polar and Al-polar AlN on 4H-SiC with 4 deg miscut using constant growth parameters. At a high temperature of 1165 degC, N-polar AlN layers had high crystalline quality whereas the Al-polar AlN surfaces had a high density of etch pits. For N-polar AlN, the V/III ratio below 1000 forms hexagonal hillocks, while the V/III ratio over 1000 yields step bunching without the hillocks. 1-um-thick N-polar AlN layer grown in optimal conditions exhibited FWHMs of 307, 330 and 337 arcsec for (002), (102) and (201) reflections, respectively.
Current browse context:
physics.app-ph
Change to browse by:
References & Citations
Bookmark
Bibliographic and Citation Tools
Bibliographic Explorer (What is the Explorer?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)
Code, Data and Media Associated with this Article
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)
Demos
Recommenders and Search Tools
Influence Flower (What are Influence Flowers?)
Connected Papers (What is Connected Papers?)
CORE Recommender (What is CORE?)
arXivLabs: experimental projects with community collaborators
arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.
Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.
Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.