Electrochemical Polishing of Chemical Vapor Deposited Niobium Thin Films
Authors:
Zeming Sun,
Mingqi Ge,
James T. Maniscalco,
Victor Arrieta,
Shawn R. McNeal,
Matthias U. Liepe
Abstract:
Combining chemical vapor deposition (CVD) with electrochemical polish (EP) operations is a promising route to producing performance-capable superconducting films for use in the fabrication of cost-effective components for superconducting radiofrequency (SRF) particle accelerators and superconducting quantum computers. The post-deposition EP process enables a critically necessary reduction in surfa…
▽ More
Combining chemical vapor deposition (CVD) with electrochemical polish (EP) operations is a promising route to producing performance-capable superconducting films for use in the fabrication of cost-effective components for superconducting radiofrequency (SRF) particle accelerators and superconducting quantum computers. The post-deposition EP process enables a critically necessary reduction in surface roughness of niobium thin films to promote optimal superconducting surface conditions. In this work, surface morphology, roughness, and crystal orientation of the CVD-grown and EP-polished niobium films were investigated. The grain growth and polishing mechanisms were analyzed. The CVD films were found to comprise steps, kinks, and pyramidal features, resulting in undesirable large peak-to-valley distances. The electrochemical polish was demonstrated to significantly diminish the height of pyramids and effectively minimize the overall surface roughness. In contrast to buffered chemical polishing (BCP), EP results showed a probable dependence on crystal orientation, suggesting this process was influenced by locally enhanced current density and thickness variations of oxide dielectrics. These understandings identify the EP principles tied to CVD-grown Nb films that allow further refinement of surface profiles for film-based SRF applications
△ Less
Submitted 2 January, 2023;
originally announced January 2023.
-
Plasma Processing for In-Situ Field Emission Mitigation of Superconducting Radiofrequency (SRF) Cryomodules
Authors:
M. Martinello,
P. Berrutti,
B. Giaccone,
S. Belomestnykh,
M. Checchin,
G. V. Eremeev,
A. Grassellino,
T. Khabibouilline,
A. Netepenko,
R. Pilipenko,
A. Romanenko,
S. Posen,
G. Wu,
D. Gonnella,
M. Ross,
J. T. Maniscalco,
T. Powers
Abstract:
Field emission (FE) is one of the main limiting factors of superconducting radio-frequency (SRF) cavities operating in accelerators and it occurs whenever contaminants, like dust, metal flakes or even absorbates, are present on the surface of the cavity high electric field region. Field emission reduces the maximum achievable accelerating field and generates free electrons that may interact with t…
▽ More
Field emission (FE) is one of the main limiting factors of superconducting radio-frequency (SRF) cavities operating in accelerators and it occurs whenever contaminants, like dust, metal flakes or even absorbates, are present on the surface of the cavity high electric field region. Field emission reduces the maximum achievable accelerating field and generates free electrons that may interact with the beam, damage or activate the beamline. One practical method that can be used to mitigate this problem is in-situ plasma cleaning, or plasma processing. The development of a processing that can be applied in-situ is extremely advantageous, since it enables the recovery of the cryomodule performance without the need of disassembling the whole cryomodule, which is an extremely expensive and time-consuming process. On the other hand, plasma processing only requires the cryomodule warm-up to room-temperature and the subsequent processing of the contaminated cavities. The entire process is reasonably quick and involves a limited number of personnel. For these reasons we would like to advocate for continuing to invest in the R\&D of plasma processing to optimize its applicability in cryomodules and for extending the technique to other frequency ranges and cavities geometries.
△ Less
Submitted 23 March, 2022;
originally announced March 2022.
-
LCLS-II-HE verification cryomodule high gradient performance and quench behavior
Authors:
S. Posen,
A. Cravatta,
M. Checchin,
S. Aderhold,
C. Adolphsen,
T. Arkan,
D. Bafia,
A. Benwell,
D. Bice,
B. Chase,
C. Contreras-Martinez,
L. Dootlittle,
J. Fuerst,
D. Gonnella,
A. Grassellino,
C. Grimm,
B. Hansen,
E. Harms,
B. Hartsell,
G. Hays,
J. Holzbauer,
S. Hoobler,
J. Kaluzny,
T. Khabiboulline,
M. Kucera
, et al. (21 additional authors not shown)
Abstract:
An 8-cavity, 1.3 GHz, LCLS-II-HE cryomodule was assembled and tested at Fermilab to verify performance before the start of production. Its cavities were processed with a novel nitrogen doping treatment to improve gradient performance. The cryomodule was tested with a modified protocol to process sporadic quenches, which were observed in LCLS-II production cryomodules and are attributed to multipac…
▽ More
An 8-cavity, 1.3 GHz, LCLS-II-HE cryomodule was assembled and tested at Fermilab to verify performance before the start of production. Its cavities were processed with a novel nitrogen doping treatment to improve gradient performance. The cryomodule was tested with a modified protocol to process sporadic quenches, which were observed in LCLS-II production cryomodules and are attributed to multipacting. Dedicated vertical test experiments support the attribution to multipacting. The verification cryomodule achieved an acceleration voltage of 200 MV in continuous wave mode, corresponding to an average accelerating gradient of 24.1 MV/m, significantly exceeding the specification of 173 MV. The average Q0 (3.0x10^10) also exceeded its specification (2.7x10^10). After processing, no field emission was observed up to the maximum gradient of each cavity. This paper reviews the cryomodule performance and discusses operational issues and mitigations implemented during the several month program.
△ Less
Submitted 27 October, 2021;
originally announced October 2021.
-
Effects of Interstitial Oxygen and Carbon on Niobium Superconducting Cavities
Authors:
P. N. Koufalis,
D. L. Hall,
M. Liepe,
J. T. Maniscalco
Abstract:
We present results on the effects of interstitial oxygen and carbon on a bulk-niobium superconducting radio-frequency cavity. Previous experiments have shown that high-temperature (~800 $^\circ\text{C}$) nitrogen-doping plays the dominant role in the reduction of the electron mean free path in the RF penetration layer of niobium that leads to a decrease in microwave surface resistance and a suppre…
▽ More
We present results on the effects of interstitial oxygen and carbon on a bulk-niobium superconducting radio-frequency cavity. Previous experiments have shown that high-temperature (~800 $^\circ\text{C}$) nitrogen-doping plays the dominant role in the reduction of the electron mean free path in the RF penetration layer of niobium that leads to a decrease in microwave surface resistance and a suppression the temperature-dependent component of the surface resistance with increasing accelerating gradient. In this work, we show that oxygen and carbon-doping has very similar effects on cavity performance, demonstrating that these effects are not unique to nitrogen. The preparation method used in the introduction of interstitial oxygen and carbon has the advantage that it is done at lower temperatures than that of high-temperature nitrogen-doping and does not require post-treatment electro-polishing.
△ Less
Submitted 31 January, 2017; v1 submitted 25 December, 2016;
originally announced December 2016.
-
The Importance of the Electron Mean Free Path for Superconducting RF Cavities
Authors:
J. T. Maniscalco,
D. Gonnella,
M. Liepe
Abstract:
Impurity-doping is an exciting new technology in the field of SRF, producing cavities with record-high quality factor $Q_0$ and BCS surface resistance that decreases with increasing RF field. Recent theoretical work has offered a promising explanation for this anti-Q-slope, but the link between the decreasing surface resistance and the short mean free path of doped cavities has remained elusive. I…
▽ More
Impurity-doping is an exciting new technology in the field of SRF, producing cavities with record-high quality factor $Q_0$ and BCS surface resistance that decreases with increasing RF field. Recent theoretical work has offered a promising explanation for this anti-Q-slope, but the link between the decreasing surface resistance and the short mean free path of doped cavities has remained elusive. In this work we investigate this link, finding that the magnitude of this decrease varies directly with the mean free path: shorter mean free paths correspond with stronger anti-Q-slopes. We draw a theoretical connection between the mean free path and the overheating of the quasiparticles, which leads to the reduction of the anti-Q-slope towards the normal Q-slope of long-mean-free-path cavities. We also investigate the sensitivity of the residual resistance to trapped magnetic flux, a property which is greatly enhanced for doped cavities, and calculate an optimal doping regime for a given amount of trapped flux.
△ Less
Submitted 5 August, 2016; v1 submitted 5 July, 2016;
originally announced July 2016.