The influence of nitrogen ion implantation on the microstructure and chemical composition of a thin layer on the biodegradable Zn-0.8Mg-0.2Sr substrate
Authors:
Jan Pinc,
Petr Vlcak,
Miroslav Lebeda,
Vilem Bartunek,
Vojtech Smola,
Marek Vronka,
Jan Drahokoupil,
Zdenek Weiss,
Petr Svora,
Hana Lesakova,
Katerina Sindelarova,
Orsolya Molnarova,
Tomas Horazdovsky,
Tomas Studecky,
Pavel Salvetr,
Jiri Kubasek,
Jaroslav Capek,
Andrea Skolakova
Abstract:
In this research, the influence of the N+ ion implantation process on the microstructure of a biodegradable Zn-0.8Mg-0.2Sr alloy was investigated using various experimental techniques. Microscopic analysis revealed that a fluence of 17x10^17 ions/cm^2 resulted in the oversaturation of pure Zn and Mg2Zn11 surfaces, leading to the formation of nano/micro-porous layers up to 400 nm thick. The behavio…
▽ More
In this research, the influence of the N+ ion implantation process on the microstructure of a biodegradable Zn-0.8Mg-0.2Sr alloy was investigated using various experimental techniques. Microscopic analysis revealed that a fluence of 17x10^17 ions/cm^2 resulted in the oversaturation of pure Zn and Mg2Zn11 surfaces, leading to the formation of nano/micro-porous layers up to 400 nm thick. The behavior of the Zn-0.8Mg-0.2Sr alloy was observed to be similar to that of the individual pure phases, albeit without the creation of pore structures. A limited formation of MgO and Mg3N2 was observed on the alloy surface, although the overall presence of Mg significantly increased from 0.8 to 15 wt.%. This increase was caused by the decomposition of the Mg2Zn11 phase during the process and subsequent diffusion of Mg toward the surface. The absence of Zn3N2 within the samples could be explained by the thermodynamic instability and low Zn-N affinity. Despite the absence of zinc nitride, GD-OES confirmed 10 at. % of nitrogen in the pure zinc, suggesting a possible accommodation of N atoms in the interstitial positions. This study points out to the complex nature of the process and highlights other promising directions for future research.
△ Less
Submitted 9 July, 2024;
originally announced July 2024.
-
Martensitic transformation induced by cooling NiTi wire under various tensile stresses: martensite variant microstructure, textures, recoverable strains and plastic strains
Authors:
O. Tyc,
X. Bian,
O. Molnárová,
L. Kadeřávek,
L. Heller,
P. Šittner
Abstract:
To understand how martensitic transformation (MT) in polycrystalline NiTi shape memory alloy (SMA) proceeds under external stress, we evaluated recoverable transformation strains and plastic strains generated by the forward MT in nanocrystalline NiTi wire cooled under tensile stresses 0-600 MPa, determined textures in martensite and reconstructed martensite variant microstructures within the selec…
▽ More
To understand how martensitic transformation (MT) in polycrystalline NiTi shape memory alloy (SMA) proceeds under external stress, we evaluated recoverable transformation strains and plastic strains generated by the forward MT in nanocrystalline NiTi wire cooled under tensile stresses 0-600 MPa, determined textures in martensite and reconstructed martensite variant microstructures within the selected grains of the cooled wire. The obtained findings show that the forward MT proceeding under external stresses gives rise to characteristic recoverable transformation strains, plastic strains, martensite variant microstructures and martensite textures. MT occurring upon cooling under stresses exceeding 100 MPa creates martensite variant microstructures consisting of single domain of partially detwinned laminate of (001) compound twins filling entire grains. The recoverable transformation strain increases with increasing stress, reaches maximum ~5% at ~200 MPa stress, and remains constant with further increasing stress up to 600 MPa. Starting from 100 MPa stress, the forward MT generates also plastic strains, the magnitude of which also increases with increasing stress. We propose that, in the absence of external stress, the forward MT takes place via propagation of strain compatible habit plane interfaces between austenite and second order laminate of (001) compound twins. When the forward MT takes place under external tensile stress, it occurs equally, but the newly created martensite immediately reorients into single domains of (001) compound twins, partially detwins and deforms plastically under the action of the external stress. The plastic strain generated by the forward MT upon cooling under stress is attributed to the [100](001) dislocation slip in martensite at low stresses and plastic deformation of martensite by kwinking at high stresses.
△ Less
Submitted 21 June, 2024;
originally announced June 2024.
-
Recoverable and plastic strains generated by forward and reverse martensitic transformations under external stress in NiTi SMA wires
Authors:
P. Šittner,
E. Iaparova,
O. Molnárová,
O. Tyc,
X. Bian,
L. Kadeřávek,
L. Heller
Abstract:
Superelastic NiTi 1 shape memory alloy (SMA) wire was subjected to thermomechanical loading tests in tension to evaluate stress and temperature conditions under which the wire deforms plastically. Although the alloy demonstrated a very high resistance to plastic deformation in both the austenite and martensite phases, incremental plastic strains were recorded whenever the B2 cubic to B19' monoclin…
▽ More
Superelastic NiTi 1 shape memory alloy (SMA) wire was subjected to thermomechanical loading tests in tension to evaluate stress and temperature conditions under which the wire deforms plastically. Although the alloy demonstrated a very high resistance to plastic deformation in both the austenite and martensite phases, incremental plastic strains were recorded whenever the B2 cubic to B19' monoclinic martensitic transformation (MT) took place under external stress. To shed light on the origin of the functional fatigue presumably originating from the accumulated plastic strains, special closed-loop thermomechanical loading tests were performed to evaluate recoverable and plastic strains generated by the forward and reverse MTs under external stress. These experiments revealed that both forward and reverse MTs generate well-defined incremental plastic strains only if they occur above certain stress thresholds. Specifically, the forward MT upon cooling under stresses up to 500 MPa does not produce plastic strain or lattice defects, whereas the reverse MT upon heating generates plastic strains even under stress as low as 100 MPa. It is proposed that plastic deformation generated by martensitic transformations under low stresses takes place by [100](001) dislocation slip in martensite and while under high stresses it occurs via kwinking deformation in martensite. The characteristic thresholds and magnitudes of plastic strains generated by the forward and reverse MTs define the functional fatigue limits for NiTi. Specifically, the stress-strain-temperature responses recorded in closed-loop thermomechanical tests remain stable if both forward and reverse MTs occur below these thresholds. Conversely, they become unstable and exhibit predictable ratcheting if the MTs exceed these thresholds.
△ Less
Submitted 21 June, 2024;
originally announced June 2024.
-
Stress induced martensitic transformation in NiTi at elevated temperatures: martensite variant microstructures, recoverable strains and plastic strains
Authors:
O. Tyc,
E. Iaparova,
O. Molnárová,
L. Heller,
P. Šittner
Abstract:
Functional behavior of NiTi shape memory alloys is restricted to temperatures below 150 °C. To shed light on the origin of the loss of functional properties of NiTi with increasing temperature, we have investigated stress induced martensitic transformations in nanocrystalline NiTi shape memory wire by thermomechanical testing supplemented with post-mortem reconstruction of martensite variant micro…
▽ More
Functional behavior of NiTi shape memory alloys is restricted to temperatures below 150 °C. To shed light on the origin of the loss of functional properties of NiTi with increasing temperature, we have investigated stress induced martensitic transformations in nanocrystalline NiTi shape memory wire by thermomechanical testing supplemented with post-mortem reconstruction of martensite variant microstructures in grains by transmission electron microscopy. It was found that the forward stress induced martensitic transformation proceeding via propagation of macroscopic Luders band fronts in stress plateaus is not completed at the end of the stress plateau and generates unrecoverable plastic strain in addition to recoverable transformation strain. The higher the test temperature, the larger is the plastic strain as well as the volume fraction of retained austenite. The reconstructed martensite variant microstructures in grains of the NiTi wire deformed up to the end of the stress plateau at 120 °C were found to be filled with single domains of (001) compound twin laminate, some grains were nearly detwinned and some grains contained (100) deformation twins. The recoverable transformation strain (~6%) generated by the forward martensitic transformation is nearly independent on the test temperature (plateau stress) because detwinning of (001) compound twins in the microstructure is prohibited by lateral constraint from the surrounding grains in nanocrystalline wire. It is concluded that the gradual loss of functionality of NiTi with increasing temperature does not originate from the plastic deformation of austenite, but that it derives from the lack of resistance of the stress induced martensite to the plastic deformation under increasing stress.
△ Less
Submitted 21 June, 2024;
originally announced June 2024.