Infrared, terahertz, and microwave spectroscopy of the soft and central modes in Pb(Mg1/3Nb2/3)O3
Authors:
D. Nuzhnyy,
J. Petzelt,
V. Bovtun,
M. Kempa,
S. Kamba,
J. Hlinka,
B. Hehlen
Abstract:
From the new infrared (IR) reflectivity and time-domain terahertz (THz) spectra combined with available high-frequency dielectric data above the MHz range in a broad temperature range of 10-900 K, a full picture of the soft and central mode behavior in the classical relaxor ferroelectric Pb(Mg1/3Nb2/3)O3 (PMN) is suggested. A detailed comparison is given with the recent hyper-Raman spectroscopy da…
▽ More
From the new infrared (IR) reflectivity and time-domain terahertz (THz) spectra combined with available high-frequency dielectric data above the MHz range in a broad temperature range of 10-900 K, a full picture of the soft and central mode behavior in the classical relaxor ferroelectric Pb(Mg1/3Nb2/3)O3 (PMN) is suggested. A detailed comparison is given with the recent hyper-Raman spectroscopy data (Phys. Rev. Lett. 117, 155501 (2016)), and also with other available experiments based on inelastic light and neutron scattering. The closest agreement is with the hyper-Raman data, both techniques yield the same number of soft-mode components and the same high-temperature softening towards the temperature T* ~ 400 K. In addition to evaluation of the IR-THz data using fitting with standard factorized form of the dielectric function, we performed a successful fitting of the same data using the effective medium approach (EMA), originally based on the assumption that the mesoscopic structure of PMN consists of randomly oriented uniaxially anisotropic polar nanodomains (PNDs) with somewhat harder TO polar modes in the direction along the local PND dipole (Phys. Rev. Lett. 96, 027601 (2006)). Evaluation using the Bruggeman EMA modelling has been successfully applied in the entire investigated temperature range. These results suggest that the response perpendicular to the local dipole moment, at high temperatures induced by random fields rather than PNDs, undergoes a classical softening from high temperatures with permittivity obeying the Curie-Weiss law, eps_per = C/(T-Tc), C = 1.7 x 10^5 K and Tc = 380 K. Below the Burns temperature ~620 K, a GHz relaxation ascribed to flipping of the PNDs emerges from the soft mode response, slows down and broadens, remaining quite strong towards the cryogenic temperatures, where it can be assigned to fluctuations of the PND boundaries.
△ Less
Submitted 18 December, 2017;
originally announced December 2017.
-
Unusual ferroelectric and magnetic phases in multiferroic 2H-BaMnO$_3$ ceramics
Authors:
Stanislav Kamba,
Dmitry Nuzhnyy,
Maxim Savinov,
Pierre Toledano,
Valentin Laguta,
Petr Brazda,
Lukas Palatinus. Filip Kadlec,
Fedir Borodavka,
Christelle Kadlec,
Petr Bednyakov,
Viktor Bovtun,
Martin Kempa,
Dominik Kriegner,
Jan Drahokoupil,
Jan Kroupa,
Jan Prokleska,
Kamal Chapagain,
Bogdan Dabrowski,
Veronica Goian
Abstract:
The structural phase transition in hexagonal BaMnO$_3$ occurring at $T_c$=130 K was studied in ceramic samples using electron and X-ray diffraction, second harmonic generation as well as by dielectric and lattice dynamic spectroscopies. The low-temperature phase (space group $P6_{3}cm$) is ferroelectric with a triplicated unit cell. The phase transition is driven by an optical soft mode from the B…
▽ More
The structural phase transition in hexagonal BaMnO$_3$ occurring at $T_c$=130 K was studied in ceramic samples using electron and X-ray diffraction, second harmonic generation as well as by dielectric and lattice dynamic spectroscopies. The low-temperature phase (space group $P6_{3}cm$) is ferroelectric with a triplicated unit cell. The phase transition is driven by an optical soft mode from the Brillouin-zone boundary [$q = (\frac{1}{3},\frac{1}{3},0)$]; this mode activates in infrared and Raman spectra below $T_c$ and it hardens according to the Cochran law. Upon cooling below $T_c$, the permittivity exhibits an unusual linear increase with temperature; below 60 K, in turn, a frequency-dependent decrease is observed, which can be explained by slowing-down of ferroelectric domain wall motions. Based on our data we could not distinguish whether the high-temperature phase is paraelectric or polar (space groups $P6_{3}/mmc$ or $P6_{3}mc$, respectively). Both variants of the phase transition to the ferroelectric phase are discussed based on the Landau theory. Electron paramagnetic resonance and magnetic susceptibility measurements reveal an onset of one-dimensional antiferromagnetic ordering below $\approx220\,\rm K$ which develops fully near 140 K and, below $T_{n} \approx 59\,\rm K$, it transforms into a three-dimensional antiferromagnetic order.
△ Less
Submitted 5 May, 2017;
originally announced May 2017.
-
Peculiar Bi-ion dynamics in Na1/2Bi1/2TiO3 from terahertz and microwave dielectric spectroscopy
Authors:
Jan Petzelt,
Dmitry Nuzhnyy,
Viktor Bovtun,
Marek Pasciak,
Stanislav Kamba,
Robert Dittmer,
Sarunas Svirskas,
Juras Banys,
Jurgen Rodel
Abstract:
Dynamics of the main dielectric anomaly in Na1/2Bi1/2TiO3 (NBT) was studied by time-domain THz and microwave spectroscopy, using also previously published data and their new overall fits. Above the dielectric maximum temperature Tm ~ 600 K, the response consists of coupled sub-THz oscillator and a relaxation mode, assigned to strongly anharmonic Bi-ion vibrations and hopping, whose slowing down ex…
▽ More
Dynamics of the main dielectric anomaly in Na1/2Bi1/2TiO3 (NBT) was studied by time-domain THz and microwave spectroscopy, using also previously published data and their new overall fits. Above the dielectric maximum temperature Tm ~ 600 K, the response consists of coupled sub-THz oscillator and a relaxation mode, assigned to strongly anharmonic Bi-ion vibrations and hopping, whose slowing down explains the paraelectric-like permittivity increase to Tm. Below Tm, the main relaxation continues slowing down and additional relaxation, assigned to quasi-Debye losses, appears in the 10^11 Hz range. The oscillator hardens on cooling and takes over the whole oscillator strength. The permittivity decrease below Tm is caused by the reduced strength of the relaxations due to dominance of the rhombohedral phase within the coexistence region with the tetragonal phase. The anharmonic dynamics of Bi is supported by previous structural studies. NBT represents a hybrid between standard and relaxor ferroelectric behaviour.
△ Less
Submitted 28 July, 2014;
originally announced July 2014.
-
Anomalous multi-order Raman scattering in LaMnO_3: a signature of a quantum lattice effect in a Jahn-Teller crystal
Authors:
N. N. Kovaleva,
O. E. Kusmartseva,
K. I. Kugel,
A. A. Maksimov,
D. Nuzhnyy,
A. M. Balbashov,
E. I. Demikhov,
A. Dejneka,
V. A. Trepakov,
F. V. Kusmartsev,
A. M. Stoneham
Abstract:
The multi-order Raman scattering is studied up to a fourth order for a detwinned LaMnO_3 crystal. Based on a comprehensive data analysis of the polarisation-dependent Raman spectra, we show that the anomalous features in the multi-order scattering could be the sidebands on the low-energy mode at about 25 cm-1. We suggest that this low-energy mode stems from the tunneling transition between the pot…
▽ More
The multi-order Raman scattering is studied up to a fourth order for a detwinned LaMnO_3 crystal. Based on a comprehensive data analysis of the polarisation-dependent Raman spectra, we show that the anomalous features in the multi-order scattering could be the sidebands on the low-energy mode at about 25 cm-1. We suggest that this low-energy mode stems from the tunneling transition between the potential energy minima arising near the Jahn-Teller Mn3+ ion due to the lattice anharmonicity, and the multi-order scattering is activated by this low-energy electronic motion. The sidebands are dominated by the oxygen contribution to the phonon density-of-states, however, there is an admixture of an additional component, which may arise from coupling between the low-energy electronic motion and the vibrational modes.
△ Less
Submitted 5 July, 2014;
originally announced July 2014.
-
Broadband dielectric spectroscopy of Ba(Zr,Ti)O3: dynamics of relaxors and diffuse ferroelectrics
Authors:
J. Petzelt,
D. Nuzhnyy,
M. Savinov,
V. Bovtun,
M. Kempa,
T. Ostapchuk,
J. Hlinka,
G. Canu,
V. Buscaglia
Abstract:
Broadband dielectric spectroscopy from Hz up to the infrared (IR) range and temperature interval 10-300 K was carried out for xBaZrO3-(1-x)BaTiO3 (BZT-x, x = 0.6, 0.7, 0.8) solid solution ceramics and compared with similar studies for x = 0, 0.2, 0.4, 1 ceramics published recently (Phys. Rev. B 86, 014106 (2012)). Rather complex IR spectra without appreciable mode softening are ascribed to Last-Sl…
▽ More
Broadband dielectric spectroscopy from Hz up to the infrared (IR) range and temperature interval 10-300 K was carried out for xBaZrO3-(1-x)BaTiO3 (BZT-x, x = 0.6, 0.7, 0.8) solid solution ceramics and compared with similar studies for x = 0, 0.2, 0.4, 1 ceramics published recently (Phys. Rev. B 86, 014106 (2012)). Rather complex IR spectra without appreciable mode softening are ascribed to Last-Slater transverse optic (TO) phonon eigenvector mixing and possible two-mode mixed crystal behavior. Fitting of the complete spectral range requires a relaxation in the 100 GHz range for all the samples. Below 1 GHz another relaxation appears, which is thermally activated and obeys the same Arrhenius behavior for all the relaxor BZT samples. The frequently reported Vogel-Fulcher behavior in BZT relaxors is shown to be an artifact of the evaluation from the permittivity or loss vs. temperature dependences instead of its evaluation from loss vs. frequency maxima. The relaxation is assigned to local hopping of the off-centered Ti4+ ions in the frozen BTO clusters, whose size is rather small and cannot grow on cooling. Therefore BZT is to be considered as a dipolar glass rather than relaxor ferroelectric.
△ Less
Submitted 11 December, 2013;
originally announced December 2013.
-
Absence of ferroelectricity in BiMnO3 ceramics
Authors:
V. Goian,
S. Kamba,
M. Savinov,
D. Nuzhnyy,
F. Borodavka,
P. Vanek,
A. A. Belik
Abstract:
We performed factor-group analysis of all phonons in possible monoclinic C2/c and C2 structures of BiMnO3 and compared it with our experimental infrared and Raman spectra. We conclude that the crystal structure is centrosymmetric C2/c in the whole investigated temperature range from 10 to 550 K, therefore BiMnO3 cannot be ferroelectric. We revealed a dielectric relaxation in THz spectra above the…
▽ More
We performed factor-group analysis of all phonons in possible monoclinic C2/c and C2 structures of BiMnO3 and compared it with our experimental infrared and Raman spectra. We conclude that the crystal structure is centrosymmetric C2/c in the whole investigated temperature range from 10 to 550 K, therefore BiMnO3 cannot be ferroelectric. We revealed a dielectric relaxation in THz spectra above the structural phase transition taking place at T_C1=475 K giving evidence in strong lattice anharmonicity and a large dynamical disorder of Bi cations above T_C1. Step-like dielectric anomaly observed at T_C1 in THz permittivity reminds antiferroelectric phase transition. Nevertheless, the low-temperature dielectric studies did not reveal any antiferroelectric or ferroelectric hysteresis loop. Our experimental results support theoretical paper of P. Baettig et al. (J. Am. Chem. Soc. 129, 9854 (2007)) claiming that BiMnO3 is not multiferroic, but only antipolar ferromagnet.
△ Less
Submitted 11 September, 2012;
originally announced September 2012.
-
Polar phonon anomalies in single crystalline TbScO3
Authors:
Stanislav Kamba,
Veronica Goian,
Dmitry Nuzhnyy,
Viktor Bovtun,
Martin Kempa,
Jan Prokleska,
Margitta Bernhagen,
Reinhard Uecker,
Darrell G. Schlom
Abstract:
Polarized infrared reflectivity spectra of a (110)-oriented TbScO3 single crystal plate were measured down to 10 K. The number of observed polar phonons active along the crystallographic c axis at low temperatures is much higher than predicted by factor-group analysis for the orthorhombic Pbnm space group. Moreover, the lowest frequency phonons active in E||c as well as in E||[1-10] polarized spec…
▽ More
Polarized infrared reflectivity spectra of a (110)-oriented TbScO3 single crystal plate were measured down to 10 K. The number of observed polar phonons active along the crystallographic c axis at low temperatures is much higher than predicted by factor-group analysis for the orthorhombic Pbnm space group. Moreover, the lowest frequency phonons active in E||c as well as in E||[1-10] polarized spectra exhibit dramatic softening tending to a lattice instability at low temperatures. The dielectric permittivity at microwave frequencies does not show any ferroelectric-like anomaly, but the dielectric loss exhibits a maximum at 100 K. The origin of the discrepancy between the number of predicted and observed polar phonons as well as the tendency toward lattice instability are discussed. Magnetic measurements reveal an antiferromagnetic phase transition near 3 K.
△ Less
Submitted 10 August, 2012;
originally announced August 2012.
-
Magnetodielectric coupling and phonon properties of compressively strained EuTiO3 thin films deposited on LSAT
Authors:
S. Kamba,
V. Goian,
M. Orlita,
D. Nuzhnyy,
J. H. Lee,
D. G. Schlom,
K. Rushchanskii,
M. Lezaic,
T. Birol,
C. J. Fennie,
P. Gemeiner,
B. Dkhil,
V. Bovtun,
M. Kempa,
J. Hlinka,
J. Petzelt
Abstract:
Compressively strained epitaxial (001) EuTiO3 thin films of tetragonal symmetry have been deposited on (001) (LaAlO3)_0.29-(SrAl_{1/2}Ta_{1/2}O3)_0.71 (LSAT) substrates by reactive molecular-beam epitaxy. Enhancement of the Neel temperature by 1 K with 0.9% compressive strain was revealed. The polar phonons ofthe films have been investigated as a function of temperature and magnetic field by means…
▽ More
Compressively strained epitaxial (001) EuTiO3 thin films of tetragonal symmetry have been deposited on (001) (LaAlO3)_0.29-(SrAl_{1/2}Ta_{1/2}O3)_0.71 (LSAT) substrates by reactive molecular-beam epitaxy. Enhancement of the Neel temperature by 1 K with 0.9% compressive strain was revealed. The polar phonons ofthe films have been investigated as a function of temperature and magnetic field by means of infrared reflectance spectroscopy. All three infrared active phonons show strongly stiffened frequencies compared to bulk EuTiO3 in accordance with first principles calculations. The phonon frequencies exhibit gradual softening on cooling leading to an increase in static permittivity. A new polar phonon with frequency near the TO1 soft mode was detected below 150 K. The new mode coupled with the TO1 mode was assigned as the optical phonon from the Brillouin zone edge, which is activated in infrared spectra due to an antiferrodistortive phase transition and due to simultaneous presence of polar and/or magnetic nanoclusters. In the antiferromagnetic phase we have observed a remarkable softening of the lowest-frequency polar phonon under an applied magnetic field, which qualitatively agrees with first principles calculations. This demonstrates the strong spin-phonon coupling in EuTiO3, which is responsible for the pronounced dependence of its static permittivity on magnetic field in the antiferromagnetic phase.
△ Less
Submitted 1 March, 2012; v1 submitted 26 January, 2012;
originally announced January 2012.
-
High-frequency dielectric spectroscopy of batio3 core - silica shell nanocomposites: Problem of interdiffusion
Authors:
D. Nuzhnyy,
J. Petzelt,
V. Bovtun,
M. Kempa,
M. Savinov,
C. Elissalde,
U-C. Chung,
D. Michau,
M. Maglione,
C. Estournes
Abstract:
Three types of BaTiO3 core - amorphous nano-shell composite ceramics were processed from the same core-shell powder by standard sintering, spark-plasma sintering and two-step sintering techniques and characterized by XRD, HRSEM and broad-band dielectric spectroscopy in the frequency range 10^3 - 10^13 Hz including the THz and IR range. The samples differed by porosity and by the amount of interdif…
▽ More
Three types of BaTiO3 core - amorphous nano-shell composite ceramics were processed from the same core-shell powder by standard sintering, spark-plasma sintering and two-step sintering techniques and characterized by XRD, HRSEM and broad-band dielectric spectroscopy in the frequency range 10^3 - 10^13 Hz including the THz and IR range. The samples differed by porosity and by the amount of interdiffusion from the cores to shells, in correlation with their increasing porosity. The dielectric spectra were also calculated using suitable models based on effective medium approximation. The measurements revealed a strong dielectric dispersion below the THz range, which cannot be explained by the modeling, and whose strength was in correlation with the degree of interdiffusion. We assigned it to an effect of the interdiffusion layers, giving rise to a strong interfacial polarization. It appears that the high-frequency dielectric spectroscopy is an extremely sensitive tool for detection of any gradient layers and sample inhomogeneities even in dielectric materials with negligible conductivity.
△ Less
Submitted 16 November, 2011;
originally announced November 2011.
-
Terahertz and Infrared Studies of Antiferroelectric Phase Transition in Multiferroic Bi_0.85Nd_0.15FeO_3
Authors:
V. Goian,
S. Kamba,
S. Greicius,
D. Nuzhnyy,
S. Karimi,
I. M. Reaney
Abstract:
High-frequency dielectric studies of Bi_0.85Nd_0.15FeO_3 ceramics performed betweeen 100 and 900 K reveal hardening of most polar phonons on cooling below antiferroelectric phase transition, which occurs near 600 K. Moreover, a strong THz dielectric relaxation is seen in paraelectric phase. Its relaxation frequency softens on cooling towards Tc ~ 600 K, its dielectric strength simultaneously decre…
▽ More
High-frequency dielectric studies of Bi_0.85Nd_0.15FeO_3 ceramics performed betweeen 100 and 900 K reveal hardening of most polar phonons on cooling below antiferroelectric phase transition, which occurs near 600 K. Moreover, a strong THz dielectric relaxation is seen in paraelectric phase. Its relaxation frequency softens on cooling towards Tc ~ 600 K, its dielectric strength simultaneously decreases and finaly the relaxation disappears from the spectra below 450 K. Both phonon and dielectric relaxation behavior is responsible for a decrease in the dielectric permittivity at the antiferroelectric phase transition. Origin of unusual strong THz dielectric relaxation in paraelectric phase is discussed. Bi_0.85Nd_0.15FeO_3 structrure lies on the phase boundary between polar rhombohedral and non-polar orthorhombic phase and owing to this the polarization rotation and polarization extension can enhance the piezoelectric response of this system. Similarities and discrepancies with lead-based piezoelectric perovskites, exhibiting morphotrophic phase boundary between two ferroelectric phases, are discussed.
△ Less
Submitted 13 October, 2011;
originally announced October 2011.
-
THz and infrared studies of multiferroic hexagonal Y_(1-x)Eu_xMnO_3 (x=0 - 0.2) ceramics
Authors:
V. Goian,
S. Kamba,
C. Kadlec,
D. Nuzhnyy,
P. Kuzel,
J. Agostinho Moreira,
A. Almeida,
P. B. Tavares
Abstract:
We report an investigation of hexagonal Y_(1-x)Eu_xMnO_3 ceramics with x=0, 0.1 and 0.2 using infrared and THz spectroscopies in the temperature range between 5 and 900 K. The temperature dependence of the THz permittivity reveals a kink near the antiferromagnetic phase transition temperature T_N ~ 70 K giving evidence of a strong spin-lattice coupling. Below T_N two absorption peaks were revealed…
▽ More
We report an investigation of hexagonal Y_(1-x)Eu_xMnO_3 ceramics with x=0, 0.1 and 0.2 using infrared and THz spectroscopies in the temperature range between 5 and 900 K. The temperature dependence of the THz permittivity reveals a kink near the antiferromagnetic phase transition temperature T_N ~ 70 K giving evidence of a strong spin-lattice coupling. Below T_N two absorption peaks were revealed in the THz spectra close to 43 and 73 cm-1. While the first peak corresponds to a sharp antiferromagnetic resonance exhibiting softening on heating towards TN, the second one may be attributed to an impurity mode or a multiphonon absorption peak. High-temperature THz spectra measured up to 900 K reveal only small gradual increase of the permittivity in agreement with a weak phonon softening observed in the infrared reflectance spectra upon heating. This corresponds to an improper ferroelectric character of the phase transition proposed from first principle calculations by Fennie and Rabe [Phys. Rev. B 72 (2005), pp. 100103(R)].
△ Less
Submitted 25 June, 2010;
originally announced June 2010.
-
First-principles design and subsequent synthesis of a material to search for the permanent electric dipole moment of the electron
Authors:
K. Z. Rushchanskii,
S. Kamba,
V. Goian,
P. Vanvek,
M. Savinov,
J. Provlevska,
D. Nuzhnyy,
K. Knivsek,
F. Laufek,
S. Eckel,
S. K. Lamoreaux,
A. O. Sushkov,
M. Lezaic,
N. A. Spaldin
Abstract:
We describe the first-principles design and subsequent synthesis of a new material with the specific functionalities required for a solid-state-based search for the permanent electric dipole moment of the electron. We show computationally that perovskite-structure europium barium titanate should exhibit the required large and pressure-dependent ferroelectric polarization, local magnetic moments, a…
▽ More
We describe the first-principles design and subsequent synthesis of a new material with the specific functionalities required for a solid-state-based search for the permanent electric dipole moment of the electron. We show computationally that perovskite-structure europium barium titanate should exhibit the required large and pressure-dependent ferroelectric polarization, local magnetic moments, and absence of magnetic ordering even at liquid helium temperature. Subsequent synthesis and characterization of Eu$_{0.5}$Ba$_{0.5}$TiO$_3$ ceramics confirm the predicted desirable properties.
△ Less
Submitted 18 June, 2010; v1 submitted 1 February, 2010;
originally announced February 2010.
-
Polar phonons in some compressively stressed epitaxial and polycrystalline SrTiO3 thin films
Authors:
D. Nuzhnyy,
J. Petzelt,
S. Kamba,
T. Yamada,
M. Tyunina,
A. K. Tagantsev,
J. Levoska,
N. Setter
Abstract:
Several SrTiO3 (STO) thin films without electrodes processed by pulsed laser deposition, of thicknesses down to 40 nm, were studied using infrared transmission and reflection spectroscopy. The complex dielectric responses of polar phonon modes, particularly ferroelectric soft mode, in the films were determined quantitatively. The compressed epitaxial STO films on (100) La0.18Sr0.82Al0.59-Ta0.41O…
▽ More
Several SrTiO3 (STO) thin films without electrodes processed by pulsed laser deposition, of thicknesses down to 40 nm, were studied using infrared transmission and reflection spectroscopy. The complex dielectric responses of polar phonon modes, particularly ferroelectric soft mode, in the films were determined quantitatively. The compressed epitaxial STO films on (100) La0.18Sr0.82Al0.59-Ta0.41O3 substrates (strain 0.9%) show strongly stiffened phonon responses, whereas the soft mode in polycrystalline film on (0001) sapphire substrate shows a strong broadening due to grain boundaries and/or other inhomogeneities and defects. The stiffened soft mode is responsible for a much lower static permittivity in the plane of the compressed film than in the bulk samples.
△ Less
Submitted 28 April, 2009;
originally announced April 2009.
-
Grain Size Influence on Dynamics of Polar Nanoclusters in PMN-35%PT Ceramics: Broadband Dielectric and Infrared Spectra
Authors:
V. Bovtun,
S. Kamba,
S. Veljko,
D. Nuzhnyy,
J. Kroupa,
M. Savinov,
P. Vanek,
J. Petzelt,
J. Holc,
M. Kosec,
H. Amorin,
M. Alguero
Abstract:
Dielectric response e*(f,T) and polar phonon spectra of coarse grain (grain size ~ 4 mkm) and fine grain (grain size ~ 150 nm) ceramics of PbMg_(1/3)Nb_(2/3)O3-35%PbTiO3 were investigated at temperatures 10 - 900 K. e*(f,T) in coarse-grain ceramics exhibits relaxor behavior at high temperatures and a sharp anomaly at the ferroelectric phase transition. The fine-grain ceramics exhibit mainly rela…
▽ More
Dielectric response e*(f,T) and polar phonon spectra of coarse grain (grain size ~ 4 mkm) and fine grain (grain size ~ 150 nm) ceramics of PbMg_(1/3)Nb_(2/3)O3-35%PbTiO3 were investigated at temperatures 10 - 900 K. e*(f,T) in coarse-grain ceramics exhibits relaxor behavior at high temperatures and a sharp anomaly at the ferroelectric phase transition. The fine-grain ceramics exhibit mainly relaxor ferroelectric behavior with a smaller dielectric constant. The difference is explained by different relaxational dynamics of polar nanoclusters, which appear to be more stabilized at high temperatures in the fine-grain ceramics by pinning at grain boundaries. Below Tc, the growth of ferroelectric domains is suppressed in fine-grain ceramics as supported also by a second harmonic generation. On the other hand, polar phonon frequencies and their temperature dependences are almost independent of the grain size, but the selection rules for the cubic symmetry are not obeyed and all phonons are split due to a locally broken symmetry by polar nanoregions and chemical disorder. The lowest-frequency polar phonon undergoes partial softening down to ~ 0.1 THz near Tc = 440 K in both ceramics, but the dielectric anomaly is caused predominantly by flipping and breathing of polar nanoclusters. Due to contribution of both the soft phonon mode and dielectric relaxations into the dielectric constant, the ferroelectric phase transition, which corresponds to the percolation threshold of the polar nanoregions into macroscopic domains, can be considered as a special case of crossover between the displacive and order-disorder type.
△ Less
Submitted 17 December, 2008;
originally announced December 2008.
-
Infrared and magnetic characterization of the multiferroic Bi2FeCrO6 thin films in a broad temperature range
Authors:
S. Kamba,
D. Nuzhnyy,
R. Nechache,
K. Zaveta,
D. Niznansky,
E. Santava,
C. Harnagea,
A. Pignolet
Abstract:
Infrared reflectance spectra of an epitaxial Bi2FeCrO6 thin film prepared by pulsed laser deposition on LaAlO3 substrate were recorded between 10 and 900 K. No evidence for a phase transition to the paraelectric phase was observed, but some phonon anomalies were revealed near 600 K. Most of the polar modes exhibit only a gradual softening, which results in a continuous increase of the static per…
▽ More
Infrared reflectance spectra of an epitaxial Bi2FeCrO6 thin film prepared by pulsed laser deposition on LaAlO3 substrate were recorded between 10 and 900 K. No evidence for a phase transition to the paraelectric phase was observed, but some phonon anomalies were revealed near 600 K. Most of the polar modes exhibit only a gradual softening, which results in a continuous increase of the static permittivity on heating. It indicates that the ferroelectric phase transition should occur somewhere above 900 K. Magnetic measurements performed up to 1000 K, revealed a possible magnetic phase transition between 600 and 800 K, but the exact critical temperature cannot be determined due to a strong diamagnetic signal from the substrate. Nevertheless, our experimental data show that the B-site ordered Bi2FeCrO6 is one of the rare high-temperature multiferroics.
△ Less
Submitted 21 December, 2007;
originally announced December 2007.
-
Dielectric relaxation and polar phonon softening in relaxor ferroelectric PbMg_(1/3)Ta_(2/3)O_3
Authors:
S. Kamba,
D. Nuzhnyy,
S. Veljko,
V. Bovtun,
J. Petzelt,
Y. L. Wang,
J. Levoska,
M. Tyunina,
J. Macutkevic,
N. Setter,
J. Banys
Abstract:
Relaxor ferroelectric PbMg_1/3Ta_2/3O_3 ceramics and thin films were investigated by means of broad-band dielectric, time-domain terahertz (THz) and Fourier-transform infrared (IR) spectroscopy in the frequency range 100 Hz - 90 THz at temperatures 100 - 490 K, the THz and IR spectra were studied from 20 to 900K. Diffused and strongly temperature dependent peak in the complex permittivity is cau…
▽ More
Relaxor ferroelectric PbMg_1/3Ta_2/3O_3 ceramics and thin films were investigated by means of broad-band dielectric, time-domain terahertz (THz) and Fourier-transform infrared (IR) spectroscopy in the frequency range 100 Hz - 90 THz at temperatures 100 - 490 K, the THz and IR spectra were studied from 20 to 900K. Diffused and strongly temperature dependent peak in the complex permittivity is caused by a dielectric relaxation due to the dynamics of polar clusters. The relaxation appears below Burns temperature T_d in the THz range, slows down on cooling through the microwave and MHz range and anomalously broadens. The shortest and longest relaxation times of the distribution of relaxation times follow Arrhenius and Vogel-Fulcher law, respectively. The degree of B-site order has only a small influence on the parameters of the dielectric relaxation and almost no influence on the phonon parameters. Below T_m ~ 180K, the distribution of relaxation frequencies becomes broader than our experimental spectral range and frequency independent dielectric losses develop below 100 GHz in the spectra. Although the macroscopic crystal structure is cubic, IR spectra give evidence about the lower local symmetry which can be assigned to the presence of polar clusters below T_d. Infrared spectra above T_d still reveal more modes than predicted by selection rules in the paraelectric phase of the Fm-3m space group so that we suggest selection rules which take into account chemical inhomogeneity in the beta''-perovskite sublattice.
△ Less
Submitted 13 July, 2007;
originally announced July 2007.
-
Magnetodielectric effect and optic soft mode behaviour in quantum paraelectric EuTiO3 ceramics
Authors:
S. Kamba,
D. Nuzhnyy,
P. Vanek,
M. Savinov,
K. Knizek,
Z. Shen,
E. Santava,
K. Maca,
M. Sadowski,
J. Petzelt
Abstract:
Infrared reflectivity and time-domain terahertz transmission spectra of EuTiO3 ceramics revealed a polar optic phonon at 6 - 300K, whose softening is fully responsible for the recently observed quantum paraelectric behaviour. Even if our EuTiO3 ceramics show lower permittivity than the single crystal due to a reduced density and/or small amount of secondary pyrochlore Eu2Ti2O7 phase, we confirme…
▽ More
Infrared reflectivity and time-domain terahertz transmission spectra of EuTiO3 ceramics revealed a polar optic phonon at 6 - 300K, whose softening is fully responsible for the recently observed quantum paraelectric behaviour. Even if our EuTiO3 ceramics show lower permittivity than the single crystal due to a reduced density and/or small amount of secondary pyrochlore Eu2Ti2O7 phase, we confirmed the magnetic field dependence of the permittivity, also slightly smaller than in single crystal. Attempt to reveal the soft phonon dependence at 1.8K on the magnetic field up to 13T remained below the accuracy of our infrared reflectivity experiment.
△ Less
Submitted 24 September, 2007; v1 submitted 13 June, 2007;
originally announced June 2007.
-
Quantum paraelectric behavior of pyrochlore PMN
Authors:
S. Kamba,
D. Nuzhnyy,
S. Denisov,
S. Veljko,
V. Bovtun,
M. Savinov,
J. Petzelt,
M. Kalnberga,
A. Sternberg
Abstract:
Pb_1.83Mg_0.29Nb_1.71O_6.39 (PMN) crystallizing in a cubic pyrochlore structure exhibits, as the first dielectrics with pyrochlore structure, typical feature of quantum paraelectrics - its permittivity continuously increases on cooling and levels off below ~ 30K, without any signature of a structural phase transition. Broad-band dielectric spectra do not show any dielectric dispersion in the rea…
▽ More
Pb_1.83Mg_0.29Nb_1.71O_6.39 (PMN) crystallizing in a cubic pyrochlore structure exhibits, as the first dielectrics with pyrochlore structure, typical feature of quantum paraelectrics - its permittivity continuously increases on cooling and levels off below ~ 30K, without any signature of a structural phase transition. Broad-band dielectric spectra do not show any dielectric dispersion in the real part of permittivity up to 8.8 GHz. THz and infrared spectra reveal a soft polar optic mode which is responsible for the temperature dependence of the permittivity. The leveling-off of the permittivity at low temperatures obeys the Barrett formula and the fitted vibrational zero-point energy 1/(2*k_B*T_1) corresponds to the measured soft mode frequency. The number of observed infrared phonons exceeds that predicted from the factor-group analysis which indicates that the structure is at least locally non-cubic.
△ Less
Submitted 12 July, 2007; v1 submitted 6 March, 2007;
originally announced March 2007.
-
Infrared and THz studies of polar phonons and improper magnetodielectric effect in multiferroic BFO3 ceramics
Authors:
S. Kamba,
D. Nuzhnyy,
M. Savinov,
J. Sebek,
J. Petzelt,
J. Prokleska,
R. Haumont,
J. Kreisel
Abstract:
BFO3 ceramics were investigated by means of infrared reflectivity and time domain THz transmission spectroscopy at temperatures 20 - 950 K, and the magnetodielectric effect was studied at 10 - 300 K, with the magnetic field up to 9 T. Below 175 K, the sum of polar phonon contributions into the permittivity corresponds to the value of measured permittivity below 1 MHz. At higher temperatures, a g…
▽ More
BFO3 ceramics were investigated by means of infrared reflectivity and time domain THz transmission spectroscopy at temperatures 20 - 950 K, and the magnetodielectric effect was studied at 10 - 300 K, with the magnetic field up to 9 T. Below 175 K, the sum of polar phonon contributions into the permittivity corresponds to the value of measured permittivity below 1 MHz. At higher temperatures, a giant low-frequency permittivity was observed, obviously due to the enhanced conductivity and possible Maxwell-Wagner contribution. Above 200 K the observed magnetodielectric effect is caused essentially through the combination of magnetoresistance and the Maxwell-Wagner effect, as recently predicted by Catalan (Appl. Phys. Lett. 88, 102902 (2006)). Since the magnetodielectric effect does not occur due to a coupling of polarization and magnetization as expected in magnetoferroelectrics, we call it improper magnetodielectric effect. Below 175 K the magnetodielectric effect is by several orders of magnitude lower due to the decreased conductivity. Several phonons exhibit gradual softening with increasing temperature, which explains the previously observed high-frequency permittivity increase on heating. The observed non-complete phonon softening seems to be the consequence of the first-order nature of the ferroelectric transition.
△ Less
Submitted 9 November, 2006; v1 submitted 1 November, 2006;
originally announced November 2006.