Crystal structure, Chemical Bonding, Electrical and Thermal Transport in Sc5Rh6Sn18
Authors:
Manuel Feig,
Lev Akselrud,
Walter Schnelle,
Vadim Dyadkin,
Dmitry Chernyshov,
Alim Ormeci,
Paul Simon,
Andreas Leithe-Jasper,
Roman Gumeniuk
Abstract:
Single crystals of Sc5Rh6Sn18 were grown from Sn-flux. The crystal structure (SG: I41/acd, a = 13.5529(2) Å, c = 27.0976(7) Å) was studied by high-resolution X-ray diffraction on powder and single crystal material as well as by TEM. All methods confirm it to crystallize with Sc5Ir6Sn18 (space group I41/acd) type of structure. The performed structural studies suggest also the presence of local doma…
▽ More
Single crystals of Sc5Rh6Sn18 were grown from Sn-flux. The crystal structure (SG: I41/acd, a = 13.5529(2) Å, c = 27.0976(7) Å) was studied by high-resolution X-ray diffraction on powder and single crystal material as well as by TEM. All methods confirm it to crystallize with Sc5Ir6Sn18 (space group I41/acd) type of structure. The performed structural studies suggest also the presence of local domains with broken average translational symmetry. Analysis of the chemical bonding situation reveal highly polar Sc2-Sn1, Sn-Rh and Sc2-Rh bonds, two- and three-center bonds involving Sn-atoms as well as ionic nature of Sc1 bonding. The thermopower of Sc5Rh6Sn18 is isotropic, small and negative (i.e. dominance of electron-like charge carriers). Due to structural disorder, the thermal conductivity is lowered in comparison with regular metallic systems.
△ Less
Submitted 30 January, 2020;
originally announced January 2020.
-
Single crystal growth of CeTAl$_3$ (T = Cu, Ag, Au, Pd and Pt)
Authors:
C. Franz,
A. Senyshyn,
A. Regnat,
C. Duvinage,
R. Schönmann,
A. Bauer,
Y. Prots,
L. Akselrud,
V. Hlukhyy,
V. Baran,
C. Pfleiderer
Abstract:
We report single crystal growth of the series of CeTAl$_3$ compounds with T = Cu, Ag, Au, Pd and Pt by means of optical float zoning. High crystalline quality was confirmed in a thorough characterization process. With the exception of CeAgAl$_3$, all compounds crystallize in the non-centrosymmetric tetragonal BaNiSn$_{3}$ structure (space group: I4mm, No. 107), whereas CeAgAl$_3$ adopts the relate…
▽ More
We report single crystal growth of the series of CeTAl$_3$ compounds with T = Cu, Ag, Au, Pd and Pt by means of optical float zoning. High crystalline quality was confirmed in a thorough characterization process. With the exception of CeAgAl$_3$, all compounds crystallize in the non-centrosymmetric tetragonal BaNiSn$_{3}$ structure (space group: I4mm, No. 107), whereas CeAgAl$_3$ adopts the related orthorhombic PbSbO$_2$Cl structure (Cmcm, No. 63). An attempt to grow CeNiAl$_3$ resulted in the composition CeNi$_2$Al$_5$. Low temperature resistivity measurements down to $\sim$0.1K did not reveal evidence suggestive of magnetic order in CePtAl$_3$ and CePdAl$_3$. In contrast, CeAuAl$_3$, CeCuAl$_3$ and CeAgAl$_3$ display signatures of magnetic transitions at 1.3K, 2.1K and 3.2K, respectively. This is consistent with previous reports of antiferromagnetic order in CeAuAl$_3$, and CeCuAl$_3$ as well as ferromagnetism in CeAgAl$_3$, respectively.
△ Less
Submitted 11 April, 2016;
originally announced April 2016.
-
Structural investigations on $ε$-FeGe at high pressure and low temperature
Authors:
H. Wilhelm,
M. Schmidt,
R. Cardoso-Gil,
U. Burkhardt,
M. Hanfland,
U. Schwarz,
L. Akselrud
Abstract:
The structural parameters of $ε$-FeGe have been determined at ambient conditions using single crystal refinement. Powder diffraction have been carried out to determine structural properties and compressibility for pressures up to 30 GPa and temperatures as low as 82 K. The discontinuous change in the pressure dependence of the shortest Fe-Ge interatomic distance might be interpreted as a symmetr…
▽ More
The structural parameters of $ε$-FeGe have been determined at ambient conditions using single crystal refinement. Powder diffraction have been carried out to determine structural properties and compressibility for pressures up to 30 GPa and temperatures as low as 82 K. The discontinuous change in the pressure dependence of the shortest Fe-Ge interatomic distance might be interpreted as a symmetry-conserving transition and seems to be related to a magnetic phase boundary line.
△ Less
Submitted 1 March, 2007;
originally announced March 2007.
-
Metallic State in Cubic FeGe beyond its Quantum Phase Transition
Authors:
P. Pedrazzini,
H. Wilhelm,
D. Jaccard,
T. Jarlborg,
M. Schmidt,
M. Hanfland,
L. Akselrud,
H. Q. Yuan,
U. Schwarz,
Yu. Grin,
F. Steglich
Abstract:
We report on results of electrical resistivity and structural investigations on the cubic modification of FeGe under high pressure. The long-wavelength helical order ($T_C=280$ K) is suppressed at a critical pressure $p_c\approx 19$ GPa. An anomaly in the resistivity data at $T_X(p)$ and strong deviations from a Fermi-liquid behavior in a wide pressure range above $p_c$ suggest that the suppress…
▽ More
We report on results of electrical resistivity and structural investigations on the cubic modification of FeGe under high pressure. The long-wavelength helical order ($T_C=280$ K) is suppressed at a critical pressure $p_c\approx 19$ GPa. An anomaly in the resistivity data at $T_X(p)$ and strong deviations from a Fermi-liquid behavior in a wide pressure range above $p_c$ suggest that the suppression of $T_C$ disagrees with the standard notion of a quantum critical phase transition. The metallic ground state persisting at high pressure can be described by band-structure calculations if structural disorder due to zero-point motion is included. Discontinuous changes in the pressure dependence of the shortest Fe-Ge interatomic distance occurring close to the $T_C(p)$ phase line could be interpreted as a symmetry-conserving transition of first order.
△ Less