Removal and Recovery of Ammonia from Wastewater using Ti$_3$C$_2$T$_x$ MXenes in Flow Electrode Capacitive Deionization
Authors:
Naqsh E Mansoor,
Luis A. Diaz,
Christopher E. Shuck,
Yury Gogotsi,
Tedd E. Lister,
David Estrada
Abstract:
Flowing electrode capacitive deionization systems (FE-CDI) have recently garnered attention because of their ability to prevent cross contamination and operate in uninterrupted cycles ad infinitum. Typically, FE-CDI electrodes suffer from low conductivity, reducing deionization performance. Utilization of higher mass loadings to combat this leads to poor rheological properties. Herein, Ti$_3$C…
▽ More
Flowing electrode capacitive deionization systems (FE-CDI) have recently garnered attention because of their ability to prevent cross contamination and operate in uninterrupted cycles ad infinitum. Typically, FE-CDI electrodes suffer from low conductivity, reducing deionization performance. Utilization of higher mass loadings to combat this leads to poor rheological properties. Herein, Ti$_3$C$_2$T$_x$ MXene was introduced as 1 mg/mL slurry electrodes in an FE-CDI system for the removal and recovery of ammonia from simulated agricultural wastewater. The electrode performance was evaluated by operating the FE-CDI system with a feed solution of 500 mg/L NH$_4$Cl running in batch mode at a constant voltage of 1.20 V and -1.20 V in charging and discharging modes, respectively. Despite the low loading, Ti$_3$C$_2$T$_x$ flowing electrodes showed markedly improved performance, achieving 60% ion removal efficiency in a saturation time of 115 minutes with an adsorption capacity of 460 mg/g. To understand the high adsorption performance of the electrodes, physiochemical and structural analysis was done via a variety of characterization techniques such as SEM, TEM, XRD, DLS, and Raman Spectroscopy. Cyclic Voltammetry and Galvanostatic charge/discharge profiles were obtained to evaluate the electrochemical properties of the electrodes. The system proved to be an energy-saving technology by exhibiting a charge efficiency of 58-70% while operating at an energy consumption of 0.45 kWh/kg. A 92% regeneration efficiency showed that the electrodes were stable and suitable for long term and scalable usage. The results demonstrate that MXenes have the potential to improve the FE-CDI process for energy-efficient removal and recovery of ammonia.
△ Less
Submitted 21 July, 2022; v1 submitted 6 July, 2020;
originally announced July 2020.
Reliability assessment in advanced nanocomposite materials for orthopaedic applications
Authors:
Jérôme Chevalier,
Paola Taddei,
Laurent Gremillard,
Sylvain Deville,
Gilbert Fantozzi,
J. F. Bartolomé,
C. Pecharroman,
J. S. Moya,
L. A. Diaz,
R. Torrecillas,
Saverio Affatato
Abstract:
Alumina-zirconia nano-composites were recently developed as alternative bearing materials for orthopedics. Previous, preliminary reports show that such alumina-zirconia nanocomposites exhibit high crack resistance and low wear rate. In this paper, additional information is given in terms of wear, crack resistance and ageing behaviour: femoral heads are inspected after 7 million cycles of wear test…
▽ More
Alumina-zirconia nano-composites were recently developed as alternative bearing materials for orthopedics. Previous, preliminary reports show that such alumina-zirconia nanocomposites exhibit high crack resistance and low wear rate. In this paper, additional information is given in terms of wear, crack resistance and ageing behaviour: femoral heads are inspected after 7 million cycles of wear testing on a hip simulator, crack resistance is measured and compared to other ceramics used today in orthopedics, slow crack growth is reported under static and cyclic fatigue, and aging resistance is assessed. We also report on the load to failure of femoral heads prototypes during compression tests. This overall reliability assessment ensures a potential future development for these kinds of new nanocomposites in the orthopedic field.
△ Less
Submitted 30 March, 2018;
originally announced April 2018.