Temperature Accelerated Life Test and Failure Analysis on Upright Metamorphic Ga0.37In0.63P/Ga0.83In0.17As/Ge Triple Junction Solar Cells
Authors:
Vincenzo Orlando,
Iván Lombardero,
Mercedes Gabás,
Neftali Nuñez,
Manuel Vázquez,
Pilar Espinet-González,
Jesús Bautista,
Rocio Romero,
Carlos Algora
Abstract:
A temperature accelerated life test on Upright Metamorphic Ga0.37In0.63P/Ga0.83In0.17As/Ge triple-junction solar cells has been carried out. The acceleration has been accomplished by subjecting the solar cells to temperatures (125, 145 and 165°C) significantly higher than the nominal working temperature inside a concentrator (90°C), while the nominal photo-current (500 suns) has been emulated by i…
▽ More
A temperature accelerated life test on Upright Metamorphic Ga0.37In0.63P/Ga0.83In0.17As/Ge triple-junction solar cells has been carried out. The acceleration has been accomplished by subjecting the solar cells to temperatures (125, 145 and 165°C) significantly higher than the nominal working temperature inside a concentrator (90°C), while the nominal photo-current (500 suns) has been emulated by injecting current in darkness. The failure distributions have been fitted to an Arrhenius-Weibull model resulting in an activation energy of 1.39 eV. Accordingly, a 72 years warranty time for those solar cells for a place like Tucson (AZ, USA), was determined. After the ALT, an intense characterization campaign has been carried out in order to determine the failure origin. We have detected that temperature soak alone is enough to degrade the cell performance by increasing the leakage currents, the series resistance, and the recombination currents. When solar cells were also forward biased an increase of series resistance together with a reduction of short circuit current is detected. The failure analysis shows that: a) several metallization sub-products concentrate in several regions of front metal grid where they poison the silver, resulting in a two times reduction of the metal sheet resistance; b) the metal/cap layer interface is greatly degraded and there is also a deterioration of the cap layer crystalline quality producing a huge increase of the specific front contact resistance, c) the decrease of short circuit current is mainly due to the GaInP top subcell degradation.
△ Less
Submitted 30 June, 2020;
originally announced June 2020.
-
Lightweight Carbon Fiber Mirrors for Solar Concentrator Applications
Authors:
Nina Vaidya,
Michael D. Kelzenberg,
Pilar Espinet-González,
Tatiana G. Vinogradova,
Jing-Shun Huang,
Christophe Leclerc,
Ali Naqavi,
Emily C. Warmann,
Sergio Pellegrino,
Harry A. Atwater
Abstract:
Lightweight parabolic mirrors for solar concentrators have been fabricated using carbon fiber reinforced polymer (CFRP) and a nanometer scale optical surface smoothing technique. The smoothing technique improved the surface roughness of the CFRP surface from ~3 μm root mean square (RMS) for as-cast to ~5 nm RMS after smoothing. The surfaces were then coated with metal, which retained the sub-wavel…
▽ More
Lightweight parabolic mirrors for solar concentrators have been fabricated using carbon fiber reinforced polymer (CFRP) and a nanometer scale optical surface smoothing technique. The smoothing technique improved the surface roughness of the CFRP surface from ~3 μm root mean square (RMS) for as-cast to ~5 nm RMS after smoothing. The surfaces were then coated with metal, which retained the sub-wavelength surface roughness, to produce a high-quality specular reflector. The mirrors were tested in an 11x geometrical concentrator configuration and achieved an optical efficiency of 78% under an AM0 solar simulator. With further development, lightweight CFRP mirrors will enable dramatic improvements in the specific power, power per unit mass, achievable for concentrated photovoltaics in space.
△ Less
Submitted 1 October, 2018;
originally announced October 2018.
-
Extremely broadband ultralight thermally emissive metasurfaces
Authors:
Ali Naqavi,
Samuel P. Loke,
Michael D. Kelzenberg,
Dennis M. Callahan,
Emily C. Warmann,
Pilar Espinet-González,
Nina Vaidya,
Tatiana A. Roy,
Jing-Shun Huang,
Tatiana G. Vinogradova,
Alexander J. Messer,
Harry A. Atwater
Abstract:
We report the design, fabrication and characterization of ultralight highly emissive metaphotonic structures with record-low mass/area that emit thermal radiation efficiently over a broad spectral (2 to 35 microns) and angular (0-60 degrees) range. The structures comprise one to three pairs of alternating nanometer-scale metallic and dielectric layers, and have measured effective 300 K hemispheric…
▽ More
We report the design, fabrication and characterization of ultralight highly emissive metaphotonic structures with record-low mass/area that emit thermal radiation efficiently over a broad spectral (2 to 35 microns) and angular (0-60 degrees) range. The structures comprise one to three pairs of alternating nanometer-scale metallic and dielectric layers, and have measured effective 300 K hemispherical emissivities of 0.7 to 0.9. To our knowledge, these structures, which are all subwavelength in thickness are the lightest reported metasurfaces with comparable infrared emissivity. The superior optical properties, together with their mechanical flexibility, low outgassing, and low areal mass, suggest that these metasurfaces are candidates for thermal management in applications demanding of ultralight flexible structures, including aerospace applications, ultralight photovoltaics, lightweight flexible electronics, and textiles for thermal insulation.
△ Less
Submitted 8 October, 2017;
originally announced October 2017.